We have investigated the damage morphology and magnetic properties of titanium dioxide thin films following implantation with Fe ions. The titanium dioxide films, having a polycrystalline anatase structure, were implanted with 100 keV Fe-56(+) ions to a total fluence of 1.3 x 10(16) ions/cm(2). The ion bombardment leads to an amorphized surface with no indication of the presence of secondary phases or Fe clusters. The ion-beam induced damage manifested itself by a marked change in surface morphology and film thickness. A room temperature ferromagnetic behaviour was observed by SQUID in the implanted sample. It is believed that the ion-beam induced damage and defects in the polycrystalline anatase film were partly responsible for the observed magnetic response.